Copolyester Optimum® 2014-XE RAUH USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | RAUH USA/Optimum® 2014-XE |
|---|---|---|---|
| Dart impact | ASTM D3763 | 36.2 J | |
| Impact strength of cantilever beam gap | ASTM D256 | 800 J/m |
| hardness | Test Condition | Test Method | RAUH USA/Optimum® 2014-XE |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 75 |
| R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | RAUH USA/Optimum® 2014-XE |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 130 % |
| Flexural modulus | ASTM D790 | 2070 MPa | |
| tensile strength | 屈服 | ASTM D638 | 55.2 MPa |
| elongation | 屈服,3.18mm | ASTM D638 | 6.5 % |
| flammability | Test Condition | Test Method | RAUH USA/Optimum® 2014-XE |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | RAUH USA/Optimum® 2014-XE |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.35 % |
| 23°C,24hr | ASTM D570 | 0.15 % | |
| density | ASTM D792 | 1.19 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | RAUH USA/Optimum® 2014-XE |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 105 °C |
| 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 95.0 °C |