ABS HH-106 INEOS STYRO THAILAND
Novodur®
Automotive interior parts、Electronic field、Application in the automo
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS STYRO THAILAND/HH-106 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 100 kJ/m² |
| 23°C | ISO 179 | 190 kJ/m² |
| Electrical performance | Test Condition | Test Method | INEOS STYRO THAILAND/HH-106 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| IEC 60093 | 1E+15 ohms·cm | ||
| dielectric strength | 1.50mm | IEC 60243-1 | 39 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | INEOS STYRO THAILAND/HH-106 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2500 Mpa | |
| ISO 527-2 | 2400 Mpa | ||
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | ISO 178 | 72.0 Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 51.0 Mpa |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ASTM D790 | 77.2 Mpa | |
| ball-indentation hardness | ISO 2039-1 | 102 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 3.0 % |
| tensile strength | 屈服,23°C | ASTM D638 | 52.0 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 9.0 % |
| Flexural modulus | ASTM D790 | 2400 Mpa |
| physical property | Test Condition | Test Method | INEOS STYRO THAILAND/HH-106 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.55 % |
| ISO 294-4 | 0.40-0.70 % | ||
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.25 % |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 7.0 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 7.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | INEOS STYRO THAILAND/HH-106 |
|---|---|---|---|
| thermal conductivity | DIN 52612 | 0.17 W/m/K | |
| vicat | -- | ISO 306/A50 | 115 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 99.0 °C |
| vicat | -- | ISO 306/B50 | 106 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,Annealed，HDT | ISO 75-2/B | 107 °C |
| maximum service temperature | 85 °C |