Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Polyolefin, Unspecified Hifax CA 207 A HMC Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | HMC Polymers/Hifax CA 207 A |
|---|---|---|---|
| Dart impact | -40°C,DuctileFailure4 | ASTM D3763 | 23.0 J |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 10 kJ/m² |
| Dart impact | 23°C,DuctileFailure5 | ASTM D3763 | 16.0 J |
| hardness | Test Condition | Test Method | HMC Polymers/Hifax CA 207 A |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | ISO 868 | 50 |
| Mechanical properties | Test Condition | Test Method | HMC Polymers/Hifax CA 207 A |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 22.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | >800 % |
| 屈服 | ISO 527-2 | 20 % | |
| tensile strength | 屈服 | ISO 527-2 | 14.0 MPa |
| Flexural modulus | ISO 178 | 500 MPa |
| physical property | Test Condition | Test Method | HMC Polymers/Hifax CA 207 A |
|---|---|---|---|
| Shrinkage rate | 48小时,3.20mm | ISO 294-4 | 0.60 % |
| density | ISO 1183/A | 0.900 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 7.5 g/10min |
| elastomer | Test Condition | Test Method | HMC Polymers/Hifax CA 207 A |
|---|---|---|---|
| tear strength | ASTM D624 | 122 kN/m |
| Thermal performance | Test Condition | Test Method | HMC Polymers/Hifax CA 207 A |
|---|---|---|---|
| vicat | ISO 306/A50 | 94.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 60.0 °C |
| melting temperature | ISO 3146 | 162 °C |