POM/PTFE C9021TF5NC CELANESE USA
HOSTAFORM®
Fitness equipment、Automotive Applications、household electrical appl、Thin walled products
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | CELANESE USA/C9021TF5NC |
|---|---|---|---|
| melt mass-flow rate | 7cm | ISO 1133 | 9.94 g/10min |
| density | ISO 1183 | 1.42 g/cm |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/C9021TF5NC |
|---|---|---|---|
| Tensile creep modulus | 1000 hours | ISO 899 part 1 | 1200 Mpa |
| Charpy without notch impact strength | 23℃ | ISO 179 1eU | 9.0 J/cm |
| elongation at break | 50mm/min | ISO 527 part 1/2 | 16 % |
| elongation | 50mm/min | ISO 527 part 1/2 | 7.0 % |
| Charpy notch impact strength | 低温-30℃ | ISO 179 1eA | 0.4 J/cm |
| Charpy without notch impact strength | 低温-30℃ | ISO 179 1eU | 8.50 J/cm |
| Tensile modulus | 1mm/min | ISO 527 part 1/2 | 2850 Mpa |
| Yield tensile strength | 50mm/min | ISO 527 part 1/2 | 53 Mpa |
| Charpy notch impact strength | 23℃ | ISO 179 1eA | 0.4 J/cm |
| ball indentation hardness | 30秒数值 | ISO 2039 part 1 | 135 Mpa |
| Tensile creep modulus | 1 hour | ISO 899 part 1 | 2400 Mpa |
| Thermal performance | Test Condition | Test Method | CELANESE USA/C9021TF5NC |
|---|---|---|---|
| 23-55℃ Longitudinal | ISO 11359 part 1/2 | 120 µm/m-℃ | |
| melting point | DSC,10 K/min | ISO 3146 method C1b | 166 °C |
| 1.8MPa | ISO 75 part 1/2 | 80 °C | |
| vicat | VST/B/50 | ISO 306 | 140 °C |