Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PARA Reny® C-36 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® C-36 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 2.647to20.893 |
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 0.975to4.365 |
| Suspended wall beam without notch impact strength | 23℃ | J/m | 0.222to0.332 |
| Impact strength of cantilever beam gap | 23℃ | J/m | 0.026to0.044 |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® C-36 |
|---|---|---|---|
| Surface Resistivity | ohms | 5.0E+3到6.0E+15 | |
| dielectric strength | 23℃ | V/mil | 500to840 |
| Compared to the Leakage Tracking Index (CTI) | V | PLC 0 | |
| Volume resistivity | 23℃ | ohms·cm | 3.0E+2到2.1E+16 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® C-36 |
|---|---|---|---|
| yield | % | 2.0to3.0 | |
| fracture | % | 1.6to2.1 | |
| 151.72to280.69 Mpa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® C-36 |
|---|---|---|---|
| Hot filament ignition temperature | °C | 798to904 |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® C-36 |
|---|---|---|---|
| balance | % | 0.70to1.5 | |
| melt mass-flow rate | 275°C/2.16kg | g/10min | 3.6to20 |
| flow | mm/mm | 38.1E-3-78.7E-3 | |
| Melt volume flow rate | 275°C/2.16kg | cm³/10min | 0.01to0.04 |
| saturation | % | 0.060to0.15 |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® C-36 |
|---|---|---|---|
| flow | mm/mm/°C | 137.2E-5-25.4E-5 | |
| horizontal | mm/mm/°C | 55.9E-5-50.8E-5 |