PC 3414R-739 SABIC INNOVATIVE JAPAN
LEXAN™
Fiber grade
Flame retardant、enhance、Glass fiber reinforced、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3414R-739 |
|---|---|---|---|
| Falling hammer impact | 23°C | ASTMD3029 | 6.78 J |
| Tensile impact strength 4 | ASTMD1822 | 67.2 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3414R-739 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ASTMD785 | 119 |
| M计秤 | ASTMD785 | 93 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3414R-739 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 3.0 % |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 186 Mpa |
| tensile strength | 断裂 | ASTMD638 | 125 Mpa |
| 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 32.0 mg | |
| Flexural modulus | 50.0mm跨距 | ASTMD790 | 9650 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3414R-739 |
|---|---|---|---|
| Volume resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| dielectric constant | 1MHz | ASTMD150 | 3.48 |
| 50Hz | ASTMD150 | 3.53 | |
| Dissipation Factor | 60Hz | ASTMD150 | 1.3E-03 |
| 50Hz | ASTMD150 | 1.3E-03 | |
| 1MHz | ASTMD150 | 6.7E-03 | |
| Arc resistance 6 | ASTMD495 | PLC7 | |
| dielectric constant | 60Hz | ASTMD150 | 3.53 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL746 | PLC 4 |
| dielectric strength | 3.20mm,inAir | ASTMD149 | 18 KV/mm |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3414R-739 |
|---|---|---|---|
| UL flame retardant rating | 1.1mm | UL94 | V-1 |
| 3.0mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3414R-739 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10to0.20 % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.23 % |
| 24hr | ASTMD570 | 0.12 % | |
| Specific volume | ASTMD792 | 0.658 cm³/g | |
| melt mass-flow rate | 300°C/5.0kg | ASTMD1238 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3414R-739 |
|---|---|---|---|
| vicat | ASTMD15255 | 166 °C | |
| MD：-40到95°C | ASTME831 | 1.6E-05 cm/cm/°C | |
| thermal conductivity | ASTMC177 | 0.22 W/m/K | |
| RTI Str | UL746 | 130 °C | |
| RTI Elec | UL746 | 130 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 146 °C | |
| RTI Imp | UL746 | 130 °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 154 °C | |
| specific heat | ASTMC351 | 1050 J/kg/°C |