PC/PBT X2500UV-YW8E099 SABIC INNOVATIVE US
XENOY™
Automotive components、Electronic and electrical
High impact、No fill
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-YW8E099 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 50 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 30 kJ/m² |
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
hardness | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-YW8E099 |
---|---|---|---|
ball-indentation hardness | H358/30 | ISO 2039-1 | 95.0 Mpa |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-YW8E099 |
---|---|---|---|
elongation | 断裂5 | ASTM D638 | 80 % |
tensile strength | 屈服5 | ASTM D638 | 56.0 Mpa |
屈服4 | ASTM D638 | 56.0 Mpa | |
elongation | 断裂4 | ASTM D638 | 80 % |
bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 79.0 Mpa |
Tensile modulus | --4 | ASTM D638 | 2200 Mpa |
--3 | ASTM D638 | 2200 Mpa | |
elongation | 断裂 | ISO 527-2/50 | 70 % |
Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2150 Mpa |
50.0mm跨距6 | ASTM D790 | 2150 Mpa | |
bending strength | --6,7 | ISO 178 | 80.0 Mpa |
tensile strength | 断裂 | ISO 527-2/50 | 56.0 Mpa |
bending strength | 屈服,50.0mm跨距6 | ASTM D790 | 79.0 Mpa |
elongation | 屈服 | ASTMD638 | 5.0 % |
tensile strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
elongation | 断裂 | ASTM D638 | 100 % |
屈服4 | ASTM D638 | 5.0 % | |
屈服5 | ASTM D638 | 5.0 % | |
tensile strength | 断裂4 | ASTM D638 | 55.0 Mpa |
断裂5 | ASTM D638 | 55.0 Mpa | |
Flexural modulus | -- | ASTM D790 | 2100 Mpa |
--6 | ISO 178 | 2150 Mpa | |
--7 | ISO 178 | 2150 Mpa | |
bending strength | -- | ASTM D790 | 79.0 Mpa |
--7,8 | ISO 178 | 80.0 Mpa | |
Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 20.0 mg |
tensile strength | 屈服 | ASTM D638 | 53.0 Mpa |
Tensile modulus | -- | ISO 527-2/1 | 2200 Mpa |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-YW8E099 |
---|---|---|---|
relative permittivity | 60Hz | IEC 60250 | 3.30 |
50Hz | IEC 60250 | 3.30 | |
Volume resistivity | IEC 60093 | >1.0E+14 ohms·cm | |
dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
relative permittivity | 1MHz | IEC 60250 | 3.10 |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
Dissipation Factor | 50Hz | IEC 60250 | 2E-03 |
60Hz | IEC 60250 | 2E-03 | |
1MHz | IEC 60250 | 0.020 |
flammability | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-YW8E099 |
---|---|---|---|
Burning wire flammability index | 2.7mm | IEC 60695-2-12 | 750 °C |
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-YW8E099 |
---|---|---|---|
Shrinkage rate | TD2 | 内部方法 | 0.50-0.80 % |
TD3 | 内部方法 | 0.50-0.80 % | |
MD:3.20mm | 内部方法 | 0.50-0.80 % | |
melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 9.0 g/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
饱和,23°C | ISO 62 | 0.70 % | |
Melt volume flow rate | 265°C/1.2kg | ISO 1133 | 4.00 cm3/10min |
Shrinkage rate | MD2 | 内部方法 | 0.50-0.80 % |
MD3 | 内部方法 | 0.50-0.80 % |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-YW8E099 |
---|---|---|---|
vicat | -- | ASTMD152512 | 135 °C |
Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 8.7E-05 cm/cm/°C |
MD:23到80°C | ISO 11359-2 | 8.2E-05 cm/cm/°C | |
Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距11,HDT | ISO 75-2/Bf | 126 °C |
1.8MPa,未退火,64.0mm跨距10,HDT | ISO 75-2/Af | 108 °C | |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
vicat | -- | ISO 306/B120 | 136 °C |
thermal conductivity | ISO 8302 | 0.18 W/m/K | |
vicat | -- | ISO 306/A50 | 145 °C |
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 8.5E-05 cm/cm/°C |
vicat | -- | ASTMD152511 | 135 °C |
Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距10,HDT | ISO 75-2/Bf | 126 °C |
1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 108 °C | |
1.8MPa,未退火,64.0mm跨距11,HDT | ISO 75-2/Af | 108 °C | |
ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |