PP TRANSMARE® 19HT20-0.001 Transmare Compounding B.V.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 19HT20-0.001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/A | 2.2 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 2.7 kJ/m² |
| hardness | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 19HT20-0.001 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 74 |
| Mechanical properties | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 19HT20-0.001 |
|---|---|---|---|
| tensile strength | 断裂,4.00mm | ISO 527-2/50 | 30.0 MPa |
| Tensile strain | 断裂,4.00mm | ISO 527-2/50 | 15 % |
| Flexural modulus | ISO 178 | 3500 MPa | |
| tensile strength | 屈服,4.00mm | ISO 527-2/50 | 35.0 MPa |
| Tensile strain | Yield,4.00mm | ISO 527-2/50 | 4.0 % |
| bending strength | ISO 178 | 59.0 MPa |
| physical property | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 19HT20-0.001 |
|---|---|---|---|
| density | ISO 1183 | 1.05 g/cm³ | |
| melt mass-flow rate | 230°C/5.0kg | ISO 1133 | 85 g/10min |
| 230°C/2.16kg | ISO 1133 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 19HT20-0.001 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 114 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 72.0 °C | |
| vicat | ISO 306/A | 154 °C |