PC Sicoklar UG10FV Entec Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Entec Polymers/Sicoklar UG10FV |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| 23°C | ISO 180/1A | 8.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Entec Polymers/Sicoklar UG10FV |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 50.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 5.0 % |
| Flexural modulus | ISO 178 | 3200 MPa |
| flammability | Test Condition | Test Method | Entec Polymers/Sicoklar UG10FV |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | 内部方法 | V-2 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | 1.6mm | 内部方法 | V-2 |
| physical property | Test Condition | Test Method | Entec Polymers/Sicoklar UG10FV |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.20to0.50 % | |
| density | ISO 1183 | 1.25 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | Entec Polymers/Sicoklar UG10FV |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 145 °C |
| BallPressureTest(125°C) | Pass | ||
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 132 °C |
| vicat | -- | ISO 306/B50 | 140 °C |