ABS TE-30 DENKA JAPAN
--
--
High impact resistance、transparent、High impact
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DENKA JAPAN/TE-30 |
|---|---|---|---|
| melt mass-flow rate | 200℃,49N | ISO 1133(JIS K7210) | 1.2 g/10min |
| density | 23℃ | ISO 1183(JIS K7112) | 1079 kg/m3 |
| melt mass-flow rate | 220℃,98N | ISO 1133(JIS K7210) | 19 g/10min |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/TE-30 |
|---|---|---|---|
| Gap Charpy impact strength | 23℃ | ISO 179(JIS K7111) | 17 kJ/m² |
| tensile yield stress | 50mm/min | ISO 527-1,-2(JIS K7161,7162) | 38 Mpa |
| Flexural modulus | 2mm/min | ISO 178(JIS K7171) | 1700 Mpa |
| Rockwell hardness | 23℃ | ISO 2039-2(JIS K7202) | 37 M |
| bending strength | 2mm/min | ISO 178(JIS K7171) | 56 Mpa |
| optical performance | Test Condition | Test Method | DENKA JAPAN/TE-30 |
|---|---|---|---|
| Total Light Transmittance | 2mmt | ISO 13468-1(JIS K7361) | 91 % |
| Haze ratio | 2mmt | ISO 14782(JIS 7136) | 1.8 % |
| physical property | Test Condition | Test Method | DENKA JAPAN/TE-30 |
|---|---|---|---|
| Shrinkage rate | DENKA Method | 0.5 % |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/TE-30 |
|---|---|---|---|
| combustibility | UL 94 | HB | |
| vicat | 50N | ISO 306(JIS K7206) | 84 °C |
| Load deformation temperature | 1.80MPa | ISO 75-1,-2(JIS K7191-1,-2) | 68 °C |