ABS HF-5 MITSUBISHI RAYON AMERICA
--
--
Having good chemical resistance, dimensional stability, impact resistance, good processing performance, good toughness, high hardness, high rigidity, high strength, and processability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Basic performance | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/HF-5 |
---|---|---|---|
Water absorption rate | 24hr | ASTM D-570 | 0.30 % |
melt mass-flow rate | 200℃/5.0kg | ASTM D-1238 | 7.0 g/10min |
Mechanical properties | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/HF-5 |
---|---|---|---|
tensile strength | 屈服,23℃ | ASTM D-638 | 40.2 MPa |
Tensile modulus | 23℃ | ASTM D-638 | 2450 MPa |
bending strength | 23℃,6.35mm,屈服 | ASTM D-790 | 62.8 MPa |
Impact strength of cantilever beam gap | 23℃,6.35mm | ASTM D-256 | 137 J/m |
Rockwell hardness | ASTM D-785 | 108 R-Scale | |
Impact strength of cantilever beam gap | -40℃,6.35mm | ASTM D-256 | 68.6 J/m |
0℃,6.35mm | ASTM D-256 | 98.1 J/m | |
Flexural modulus | 23℃,6.35mm | ASTM D-790 | 2450 MPa |
physical property | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/HF-5 |
---|---|---|---|
density | ASTM D-792 | 1.05 g/cm | |
Shrinkage rate | Flow | ASTM D-955 | 0.50 % |
Thermal performance | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/HF-5 |
---|---|---|---|
Heat distortion temperature | 1.80MPa,未退火,12.7mm,HDT | ASTM D-648 | 88.0 ℃ |
specific heat | ASTM C-351 | 1670 J/kg/℃ | |
UL flame retardant rating | NC | UL 94 | HB |
Linear coefficient of thermal expansion | Flow | ASTM D-696 | 0.000085 cm/cm/℃ |
thermal conductivity | ASTM C-177 | 0.21 W/m.K |