PA66 FR200 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 ASAHI JAPAN FR200

Injection grade

US$ 4,410 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	ASAHI JAPAN/FR200
elongation	Break	ASTM D638	25 %
Rockwell hardness	干(湿)	ASTM D-785	118(90) M Scale
bending strength	23°C	ISO 178	117 Mpa
bending strength		干(湿)	ASTM D-790	118(44) Mpa
tensile strength		ASTM D638	79.0 Mpa
bending strength		ASTM D790/ISO 178	118(MPa) kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	R118
Bending modulus		ASTM D790/ISO 178	2940(MPa) kg·cm/cm(J/M)ft·lb/in
Tensile modulus	23°C	ISO 527-2	3500 Mpa
Tensile strain	Break,23°C	ISO 527-2	10 %
Taber abraser	1000Cycles	ASTM D1044	-- mg
tensile strength	Yield,23°C	ISO 527-2	75.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.5 %
tensile strength	Break,23°C	ISO 527-2	69.0 Mpa
bending strength		ASTM D790	118 Mpa
tensile strength	干(湿)	ASTM D-638	79(47) Mpa
flexural coefficient	干(湿)	ASTM D-790	2.9(1.1) GPa
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	29(118) J/m
Bending modulus	23°C	ISO 178	2900 Mpa
Bending modulus			ASTM D790	2900 Mpa
Elongation at Break	干(湿)	ASTM D-638	25(80) %
Electrical performance	Test Condition	Test Method	ASAHI JAPAN/FR200
Arc resistance		ASTM D495/IEC 60112	124
Volume resistivity	23°C	IEC 60093	1E+14 ohms·cm
Surface resistivity		ASTM D257	1E+13 ohms
Surface resistivity			IEC 60093	1E+13 ohms
Dielectric strength		IEC 60243-1	19 KV/mm
Dielectric strength			ASTM D149	19 KV/mm
Volume resistivity		ASTM D257	1E+14 ohms·cm
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 0
other	Test Condition	Test Method	ASAHI JAPAN/FR200
characteristic			难燃性
thermal performance	Test Condition	Test Method	ASAHI JAPAN/FR200
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	8 mm/mm.℃
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	209 °C
UL flame retardant rating	干	UL 94	V-0
thermal conductivity			0.20 W/m/K
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	62.0 °C
		HDT	ASTM D648/ISO 75	209 ℃（℉）
		0.46MPa,干	ASTM D-648	209 °C
		1.82MPa,干	ASTM D-648	66 °C
specific heat			1670 J/kg/°C
Linear coefficient of thermal expansion	MD	ASTM D696	8E-05 cm/cm/°C
thermal conductivity	干		0.2 W/(m.K)
Linear coefficient of thermal expansion	干	ASTM D-696	8
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	203 °C
Hot deformation temperature		1.8MPa,Unannealed	ASTM D648	66.0 °C
Combustibility (rate)		UL 94	V-0
specific heat	干		1670 J/(kg.k)
flammability	Test Condition	Test Method	ASAHI JAPAN/FR200
Extreme Oxygen Index		ASTM D2863	32 %
UL flame retardant rating	0.75mm	UL 94	V-0
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Physical properties	Test Condition	Test Method	ASAHI JAPAN/FR200
Shrinkage rate	干	旭化成方法	1.3-2.0 %
			ASTM D955	1.3-2.0 %
		MD	Internal Method	1.3-2.0 %
density		ASTM D792/ISO 1183	1.16
Water absorption rate		ASTM D570/ISO 62	2.4 %
Wear factor	湿	ASTM D-1044	8
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	-- %
Water absorption rate		Saturation,23°C		-- %
hardness	Test Condition	Test Method	ASAHI JAPAN/FR200
Rockwell hardness	M-Sale	ISO 2039-2	80
		R-Sale	ASTM D785	118
		M-Sale	ASTM D785	80
		R-Sale	ISO 2039-2	118
Basic Performance	Test Condition	Test Method	ASAHI JAPAN/FR200
Water absorption rate	湿		2.4 %
Other performance	Test Condition	Test Method	ASAHI JAPAN/FR200
Extreme Oxygen Index	干	ASTM D-2863	32 %
impact performance	Test Condition	Test Method	ASAHI JAPAN/FR200
Impact strength of simply supported beam without notch		ISO 179	NoBreak