Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF-3200H Samsung Cheil South Korea
INFINO®
Automotive components、Home appliance components
High temperature resistan、UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/HF-3200H |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 12 kJ/m² |
| 23°C,3.18mm | ASTM D256 | 140 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/HF-3200H |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 118 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/HF-3200H |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 4800 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 110 Mpa |
| elongation | 断裂 | ASTM D638 | 4.3 % |
| Tensile modulus | ISO 527-2/50 | 5100 Mpa | |
| bending strength | ISO 178 | 170 Mpa | |
| Flexural modulus | ISO 178 | 5800 Mpa | |
| bending strength | ASTM D790 | 120 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 110 Mpa |
| 屈服 | ASTM D638 | 78.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 3.7 % |
| Flexural modulus | ASTM D790 | 4600 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 115 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/HF-3200H |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/HF-3200H |
|---|---|---|---|
| ash content | ISO 3451 | 19 % | |
| density | ASTM D792 | 1.37 g/cm³ | |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 11 g/10min |
| density | ISO 1183 | 1.37 g/cm³ | |
| melt mass-flow rate | 250°C/10.0kg | ISO 1133 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/HF-3200H |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 142 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 140 °C | |
| vicat | -- | ISO 306/B120 | 150 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 146 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 142 °C | |
| vicat | -- | ISO 306/B50 | 150147 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 145 °C |
| 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 146 °C |