PC 3414R-131 SABIC INNOVATIVE US
LEXAN™
Fiber grade
Flame retardant,enhance,Glass fiber reinforced,High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/3414R-131 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | －－ Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 3.48 | |
| Dielectric loss | ASTM D150/IEC 60250 | 0.0067 | |
| arc resistance | ASTM D495/IEC 60112 | －－ | |
| Volume resistivity | ASTM D257/IEC 60093 | >1.0E+17 ohm.cm Ω.cm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/3414R-131 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | －－ kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 27000 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 1.40E+6 PSI kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | －－ % | |
| Tensile modulus | ASTM D638/ISO 527 | －－ kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | －－ kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 3.0 % | |
| Rockwell hardness | ASTM D785 | M-93.R-119 | |
| tensile strength | ASTM D638/ISO 527 | 23000 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | SABIC INNOVATIVE US/3414R-131 |
|---|---|---|---|
| characteristic | 加纤40%.加脱模剂 | ||
| notes | 注射成型 | ||
| Color | 本色 | ||
| purpose | －－ |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/3414R-131 |
|---|---|---|---|
| Fuzzy coefficient (Haze) | ISO 14782 | －－ % | |
| refractive index | ASTM D542/ISO 489 | －－ | |
| transmittance | ASTM D1003/ISO 13468 | －－ % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/3414R-131 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.1－0.2 % | |
| density | ASTM D792/ISO 1183 | 1.52－1.53 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 300℃/5.0kg.13 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.12 % |
| processability | Test Condition | Test Method | SABIC INNOVATIVE US/3414R-131 |
|---|---|---|---|
| process temperature | 560－620 °C | ||
| pressure | 50.0－100 Mpa | ||
| Dry conditions | 干燥温度：250℉.干燥时间：3.0to4.0 hr | ||
| screw speed | 40－70 rpm | ||
| Melt Temperature | 600－640 °C | ||
| Temperature | 180－240 °C |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/3414R-131 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-1-V-0 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | －－ ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 330 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 9.0E-6 in/in/℉ mm/mm.℃ |