Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TP, Unspecified Hapflex™ 669-3 HAPCO USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | HAPCO USA/Hapflex™ 669-3 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 无断裂 | |
| Impact strength of cantilever beam gap | ASTM D256 | 120 J/m |
| hardness | Test Condition | Test Method | HAPCO USA/Hapflex™ 669-3 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 65 |
| Mechanical properties | Test Condition | Test Method | HAPCO USA/Hapflex™ 669-3 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 100 % |
| tensile strength | ASTM D638 | 22.8 MPa | |
| Flexural modulus | ASTM D790 | 283 MPa | |
| Tensile modulus | ASTM D638 | 172 MPa | |
| bending strength | ASTM D790 | 18.6 MPa |
| thermosetting | Test Condition | Test Method | HAPCO USA/Hapflex™ 669-3 |
|---|---|---|---|
| Thermosetting mixed viscosity | 25°C | ASTM D4878 | 2550 cP |
| GelTime | 25°C | ASTM D2971 | 3.0 min |
| stripping time | 21°C | 内部方法 | 10to20 min |
| Thermosetting components | 部件A | 按重量计算的混合比:100.按容量计算的混合比:100 | |
| 部件B | 按重量计算的混合比:50.按容量计算的混合比:50 |
| elastomer | Test Condition | Test Method | HAPCO USA/Hapflex™ 669-3 |
|---|---|---|---|
| tear strength | ASTM D624 | 78.8 kN/m |
| physical property | Test Condition | Test Method | HAPCO USA/Hapflex™ 669-3 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D2566 | 0.30to0.50 % |
| density | ASTM D4669 | 1.10 g/cm³ | |
| Weight Percubicinch | 17 g |
| Thermal performance | Test Condition | Test Method | HAPCO USA/Hapflex™ 669-3 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 71.0 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 110 °C |