HDPE AEI SX-0410:CM401 UK AEI Compounds
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | UK AEI Compounds/AEI SX-0410:CM401 |
|---|---|---|---|
| CureTime | 1.50mm | 14.0 day | |
| 800.0µm | 5.0 day |
| Mechanical properties | Test Condition | Test Method | UK AEI Compounds/AEI SX-0410:CM401 |
|---|---|---|---|
| tensile strength | IEC 60811-1-1 | 19.0 MPa | |
| Tensile strain | 断裂 | IEC 60811-1-1 | 450 % |
| Electrical performance | Test Condition | Test Method | UK AEI Compounds/AEI SX-0410:CM401 |
|---|---|---|---|
| Volume resistivity | 20°C | BS6622 | >1.0E+16 ohms·cm |
| Loss factor | 23°C | IEC 60250 | 3E-04 |
| relative permittivity | 23°C,50Hz | IEC 60250 | 2.00 |
| dielectric strength | 20°C | IEC 60243-1 | 21 kV/mm |
| physical property | Test Condition | Test Method | UK AEI Compounds/AEI SX-0410:CM401 |
|---|---|---|---|
| density | BS2782620A | 0.930 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | 内部方法 | 1.4 g/10min |
| aging | Test Condition | Test Method | UK AEI Compounds/AEI SX-0410:CM401 |
|---|---|---|---|
| Change rate of tensile strength in air | 135°C,168hr | IEC 60811-1-2 | 7.0 % |
| Tensile stress change rate | 135°C,168hr，断裂 | IEC 60811-1-2 | -7.0 % |
| Thermal performance | Test Condition | Test Method | UK AEI Compounds/AEI SX-0410:CM401 |
|---|---|---|---|
| Cold bend | -70°C | IEC 60811-1-4 | pass |
| thermosetting | Elongationunderload,20N/cm²:200°C | IEC 60811-2-1 | <100 % |
| Permanentelongationaftercooling | IEC 60811-2-1 | 0.0 % |