Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POP PL 1850G DOW THAILAND
AFFINITY™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | DOW THAILAND/PL 1850G |
|---|---|---|---|
| Thin film puncture strength | 20µm | 内部方法 | 31.4 J/cm³ |
| Dart impact | 20µm | ASTM D1709B | >830 g |
| Secant modulus | 2%正割,TD:20µm | ASTM D882 | 115 Mpa |
| tensile strength | TD:断裂,20µm | ASTM D882 | 29.8 Mpa |
| elongation | MD:断裂,20µm | ASTM D882 | 350 % |
| tensile strength | TD:屈服,20µm | ASTM D882 | 5.45 Mpa |
| MD:断裂,20µm | ASTM D882 | 44.6 Mpa | |
| Secant modulus | 2%正割,MD:20µm | ASTM D882 | 108 Mpa |
| Elmendorf tear strength | TD:20µm | ASTM D1922 | 410 g |
| tensile strength | MD:屈服,20µm | ASTM D882 | 9.93 Mpa |
| Initial sealing temperature | 20µm | 内部方法 | 93.9 °C |
| elongation | TD:断裂,20µm | ASTM D882 | 570 % |
| film thickness | 20 µm | ||
| Elmendorf tear strength | MD:20µm | ASTM D1922 | 120 g |
| Thin film puncture strength | 20µm | 内部方法 | 4.28 J |
| 20µm | 内部方法 | 47.6 N |
| thermal performance | Test Condition | Test Method | DOW THAILAND/PL 1850G |
|---|---|---|---|
| melting temperature | 内部方法 | 98.0 °C | |
| vicat | ASTM D1525 | 85.0 °C |
| optical performance | Test Condition | Test Method | DOW THAILAND/PL 1850G |
|---|---|---|---|
| gloss | 20°,20.3µm | ASTM D2457 | 144 |
| Haze ratio | 20.3µm | ASTM D1003 | 0.70 % |
| Physical properties | Test Condition | Test Method | DOW THAILAND/PL 1850G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 3.0 g/10min |