Melt Volume-Flow Rate (MVR)

220°C/5.0kg

ISO1133

cm3/10min

2

Melt mass flow rate

220°C/10.0kg

ASTMD1238

g/10min

9

Shrinkage rate

MD：3.20mm

内部方法

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Impact strength of simply supported beam gap

23°C

ISO179/1eA

kJ/m²

1

Tensile modulus

ASTMD638

Mpa

1

Tensile modulus

ISO527-2/1

Mpa

1

tensile strength

屈服

ASTMD638

Mpa

3

tensile strength

屈服

ISO527-2/50

Mpa

3

tensile strength

断裂

ASTMD638

Mpa

3

tensile strength

断裂

ISO527-2/50

Mpa

2

elongation

屈服

ASTMD638

%

3

elongation

屈服

ISO527-2/50

%

3

elongation

断裂

ASTMD638

%

3

elongation

断裂

ISO527-2/50

%

2

Bending modulus

50.0mm跨距

ASTMD790

Mpa

1

Bending modulus

ISO178

Mpa

1

bending strength

屈服,50.0mm跨距

ASTMD790

Mpa

5

Bending strength 5,

ISO178

Mpa

5

Suspended wall beam gap impact strength

-30°C

ISO180/1A

kJ/m²

7

Suspended wall beam gap impact strength

23°C

ISO180/1A

kJ/m²

1

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

2

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

6

Hot deformation temperature

1.8MPa,Unannealed,64.0mmSpan

ISO75-2/Af

°C

7

vicat softening point

--

ISO306/B120

°C

8

vicat softening point

ASTMD152510

°C

8

vicat softening point

--

ISO306/B50

°C

8

Linear coefficient of thermal expansion

MD：-40到40°C

ASTME831

cm/cm/°C

9

Linear coefficient of thermal expansion

MD：-40到40°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：-40到40°C

ASTME831

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：-40到40°C

ISO11359-2

cm/cm/°C

1