PA6 PLUSTEK PB305G33BK37/43 POLYRAM ISRAEL
--
--
Filler, glass fiber reinforced material, 33%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PB305G33BK37/43 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 200 J/m |
| 23°C | ISO 180 | 17 kJ/m² |
| hardness | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PB305G33BK37/43 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 113 |
| R级 | ASTM D785 | 113 |
| Electrical performance | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PB305G33BK37/43 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 80 kV/mm | |
| Volume resistivity | IEC 60093 | 1E+17 ohms·cm | |
| dielectric constant | 1MHz | IEC 60250 | 3.80 |
| Surface Resistivity | IEC 60093 | 1E+12 ohms |
| Mechanical properties | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PB305G33BK37/43 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 3.5 % |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| Flexural modulus | ASTM D790 | 9000 MPa | |
| Tensile modulus | ASTM D638 | 10000 MPa | |
| ISO 527-2 | 10000 MPa | ||
| tensile strength | 屈服 | ASTM D638 | 180 MPa |
| 屈服 | ISO 527-2 | 180 MPa | |
| Flexural modulus | ISO 178 | 9000 MPa | |
| bending strength | ASTM D790 | 250 MPa | |
| ISO 178 | 250 MPa |
| flammability | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PB305G33BK37/43 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PB305G33BK37/43 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.20to0.50 % | |
| MD | ASTM D955 | 0.20to0.50 % | |
| Water absorption rate | 饱和 | ASTM D570 | 6.6 % |
| 平衡,23°C,50%RH | ASTM D570 | 2.1 % | |
| 平衡,23°C,50%RH | ISO 62 | 2.1 % | |
| 饱和,23°C | ISO 62 | 6.6 % | |
| density | ASTM D792 | 1.37 g/cm³ | |
| ISO 1183 | 1.37 g/cm³ |
| Thermal performance | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PB305G33BK37/43 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 218 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 205 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 217 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 217 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C | |
| melting temperature | ASTM D3418 | 218 °C | |
| Continuous use temperature | 110 °C | ||
| maximum service temperature | 200 °C |