Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS C3650-111 SABIC INNOVATIVE SINGAPHORE
CYCOLOY™
Shell、Electronic and electrical
High mobility、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/C3650-111
Melt Volume-Flow Rate (MVR)
260°C/5.0kg
ISO1133
cm3/10min
8
Melt mass flow rate
260°C/5.0kg
ASTMD1238
g/10min
8
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/C3650-111
Impact strength of simply supported beam gap
-30°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam gap
23°C
ISO179/1eA
kJ/m²
4
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
tensile strength
屈服
ASTMD638
Mpa
6
tensile strength
屈服
ISO527-2/5
Mpa
5
tensile strength
屈服
ISO527-2/50
Mpa
6
tensile strength
断裂
ASTMD638
Mpa
5
tensile strength
断裂
ISO527-2/5
Mpa
5
tensile strength
断裂
ISO527-2/50
Mpa
5
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1
elongation
屈服
ASTMD638
%
4
elongation
屈服
ISO527-2/5
%
3
elongation
屈服
ISO527-2/50
%
4
elongation
断裂
ASTMD638
%
3
elongation
断裂
ISO527-2/5
%
5
elongation
断裂
ISO527-2/50
%
>
Bending modulus
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
1
Bending strength 5,
ISO178
Mpa
1
Suspended wall beam gap impact strength
-30°C
ISO180/1A
kJ/m²
1
Suspended wall beam gap impact strength
0°C
ISO180/1A
kJ/m²
1
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
4
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
6
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/C3650-111
RTI Imp
UL746
°C
6
RTIElec
UL746
°C
6
RTIStr
UL746
°C
6
thermal conductivity
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
9
vicat softening point
ASTMD152510
°C
1
vicat softening point
--
ISO306/B50
°C
1
vicat softening point
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：23到60°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：23to60°C
ISO11359-2
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/C3650-111
Surface resistivity
IEC60093
ohms
>
Dielectric strength
0.800mm,在油中
IEC60243-1
KV/mm
3
Dielectric strength
1.60mm,在油中
IEC60243-1
KV/mm
2
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
>
flammability
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/C3650-111
Extreme Oxygen Index
ISO4589-2
%
3