Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PC/PBT X2420 BK1066 SABIC INNOVATIVE NANSHA
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/X2420 BK1066 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
23°C | ISO 180/1A | 14 kJ/m² | |
ISO 180/1U | 110 kJ/m² | ||
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 36.0 J |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
23°C | ASTM D256 | 210 J/m | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 95 kJ/m² |
-30°C | ISO 180/1A | 8.0 kJ/m² | |
23°C | ASTM D4812 | 1600 J/m | |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 95 kJ/m² |
-30°C | ISO 180/1U | 74 kJ/m² |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/X2420 BK1066 |
---|---|---|---|
Tensile modulus | ASTM D638 | 3800 Mpa | |
bending strength | 屈服,50.0mm跨距 | ASTM D790 | 90.0 Mpa |
yield | ASTM D638 | 50.0 Mpa | |
fracture | ISO 527-2/5 | 37.0 Mpa | |
yield | ASTM D638 | 3.0 % | |
ISO 527-2/5 | 51.0 Mpa | ||
ISO 527-2/5 | 3.0 % | ||
fracture | ASTM D638 | 35.0 Mpa | |
ISO 527-2/5 | 7.0 % | ||
Flexural modulus | 50.0mm跨距 | ASTM D790 | 3500 Mpa |
flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/X2420 BK1066 |
---|---|---|---|
UL flame retardant rating | 0.400mm | UL 94 | HB |
physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/X2420 BK1066 |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.15-0.25 % |
Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 26.0 cm3/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.040 % |
饱和,23°C | ISO 62 | 0.020 % | |
Shrinkage rate | TD:3.20mm | 内部方法 | 0.30-0.40 % |
Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/X2420 BK1066 |
---|---|---|---|
Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 4E-05 cm/cm/°C |
vicat | ISO 306/B120 | 118 °C | |
Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 9E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 111 °C |
Flow: -40 to 40 ° C | ASTME831 | 5E-05 cm/cm/°C | |
Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 8E-05 cm/cm/°C |
RTI Imp | UL 746 | 75.0 °C | |
RTI | UL 746 | 75.0 °C | |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 101 °C |
RTI Elec | UL 746 | 75.0 °C |