PC/ABS T88GF30 901510 COVESTRO SHANGHAI
Bayblend®
Automotive Applications、Electrical applications、household electrical appl
heat-resisting、Flame retardant、Filler: Glass fiber reinf、31% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF30 901510 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 40 kJ/m² |
| -30°C | ISO 180 | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF30 901510 |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.40 |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.60 |
| Surface Resistivity | IEC 60093 | 1E+17 ohms | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 3E-03 |
| 23°C,1MHz | IEC 60250 | 8.5E-03 |
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF30 901510 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.0 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 135 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 10000 Mpa |
| flammability | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF30 901510 |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | UL 94 | HB |
| physical property | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF30 901510 |
|---|---|---|---|
| MeltViscosity | 260°C | ISO 11443-A | 250 Pa·s |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Shrinkage rate | MD:260°C,3.00mm | ISO 2577 | 0.15-0.35 % |
| TD:260°C,3.00mm | ISO 2577 | 0.30-0.50 % |
| Thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF30 901510 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 134 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 134 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 126 °C |
| vicat | -- | ISO 306/B50 | 132 °C |