Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF1140-111FC SABIC INNOVATIVE NANSHA
LEXAN™
chip,container,Thin walled products,Safety equipment,Optical data storage,lens
High mobility,Good demolding performanc,Good forming performance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| -30°C | ISO 179/1eA | 10 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 54.0 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 378 kJ/m² | |
| Dart impact | 23°C | ASTM D3029 | 169 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 70 |
| R 级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2370 Mpa |
| tensile strength | 屈服3 | ASTM D638 | 62.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 120 % |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
| elongation | 断裂 | ISO 527-2/50 | 70 % |
| Flexural modulus | --5 | ISO 178 | 2300 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 93.0 Mpa |
| --5,6 | ISO 178 | 90.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2300 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| 屈服3 | ASTM D638 | 6.0 % | |
| tensile strength | 断裂3 | ASTM D638 | 65.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2350 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| Volume resistivity | -- | ASTM D257 | > 1.0E+17 ohms·cm |
| dielectric constant | 50 Hz | IEC 60250 | 2.70 |
| Dissipation Factor | 50 Hz | ASTM D150 | 9.0E-4 |
| dielectric constant | 1 MHz | ASTM D150 | 2.96 |
| Dissipation Factor | 50 Hz | IEC 60250 | 1.0E-3 |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 1 | |
| dielectric constant | 60 Hz | IEC 60250 | 2.70 |
| 60 Hz | ASTM D150 | 3.17 | |
| Dissipation Factor | 60 Hz | ASTM D150 | 9.0E-4 |
| Volume resistivity | -- | IEC 60093 | > 1.0E+15 ohms·cm |
| Dissipation Factor | 60 Hz | IEC 60250 | 1.0E-3 |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 15 KV/mm |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.010 |
| dielectric constant | 50 kHz | ASTM D150 | 3.17 |
| 1 MHz | IEC 60250 | 2.70 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | 2540 µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 |
| Limiting Oxygen Index | ISO 4589-2 | 25 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.35 % |
| 平衡, 100°C | ASTM D570 | 0.58 % | |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 23.0 cm3/10min |
| Water absorption rate | 24 hr | ASTM D570 | 0.15 % |
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 25 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距11，HDT | ISO 75-2/Be | 133 °C |
| thermal conductivity | -- | ASTM C177 | 0.19 W/m/K |
| Linear coefficient of thermal expansion | -40 到 95°C，流动 | ASTM E831 | 6.8E-5 cm/cm/°C |
| specific heat | ASTM C351 | 1250 J/kg/°C | |
| thermal conductivity | -- | ISO 8302 | 0.20 W/m/K |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI | UL 746 | 130 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 137 °C |
| vicat | -- | ISO 306/B120 | 140 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距11，HDT | ISO 75-2/Ae | 121 °C |
| vicat | -- | ISO 306/B50 | 139 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 126 °C |
| RTI Imp | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | 23 到 80°C，流动 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 126 °C |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1140-111FC |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 270 to 295 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 260 to 280 °C | ||
| Temperature at the rear of the barrel | 250 to 270 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 270 to 295 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 95 °C | ||
| Spray nozzle temperature | 265 to 290 °C |