PBT 313RA ED3002 JAPAN POLYPLASTIC
DURANEX®
--
Good adhesion,15%GF,Filler: Glass fiber reinf,15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/313RA ED3002 |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/313RA ED3002 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Volume resistivity | IEC 60093 | 2E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 24 KV/mm |
| Volume resistivity | IEC 60093 | 2×10 Ω.cm | |
| Surface Resistivity | IEC 60093 | 2×10 Ω |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/313RA ED3002 |
|---|---|---|---|
| tensile strength | ISO 527-1/-2 | 110 Mpa | |
| bending strength | ISO 178 | 160 Mpa | |
| Flexural modulus | ISO 178 | 5330 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Charpy Notched Impact Strength | ISO 179/1eA | 6.0 KJ/m | |
| tensile strength | ISO 527-2 | 110 Mpa |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/313RA ED3002 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/313RA ED3002 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/313RA ED3002 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 197 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | 内部方法 | 4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 197 °C |
| UL flame retardant rating | UL 94 | HB |