Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LS-3302 Samsung Cheil South Korea
INFINO®
Automotive components、Electronic and electrical
Thermal stability、High mobility、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/LS-3302 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 12 kJ/m² |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/LS-3302 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 120 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/LS-3302 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 7000 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 120 Mpa |
| elongation | 断裂 | ASTM D638 | 4.0 % |
| Tensile modulus | ISO 527-2/50 | 6600 Mpa | |
| bending strength | ISO 178 | 175 Mpa | |
| Flexural modulus | ISO 178 | 8300 Mpa | |
| bending strength | ASTM D790 | 180 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 130 Mpa |
| 屈服 | ASTM D638 | 130 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 3.0 % |
| Flexural modulus | ASTM D790 | 7400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 120 Mpa |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/LS-3302 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.24-0.30 % |
| TD:3.20mm | ISO 2577 | 0.29-0.35 % | |
| TD：3.20mm | ASTM D955 | 0.29-0.35 % | |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 12 g/10min |
| 250°C/10.0kg | ISO 1133 | 12 g/10min | |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.24-0.30 % |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/LS-3302 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 140 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 140 °C | |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 144 °C | |
| vicat | ISO 306/B50 | 149148 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 144 °C |