Product Name / Manufacturer / Model

Grade

Reference Price

PBT BASF GERMANY B 4406

Injection grade

US$ 3,790 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	BASF GERMANY/B 4406
Tensile creep modulus	1hr	ISO 899-1	1800 Mpa
tensile strength	Yield,23°C	ASTM D638	65.0 Mpa
elongation	Yield,23°C	ASTM D638	3.9 %
Tensile modulus	23°C	ISO 527-2	3000 Mpa
tensile strength	Yield,23°C	ISO 527-2	65.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.9 %
Tensile modulus		ASTM D638/ISO 527	3000 kg/cm²(MPa)[Lb/in²]
Nominal tensile fracture strain	-40°C	ISO 527-2	3.3 %
Nominal tensile fracture strain		23°C	ISO 527-2	3.5 %
thermal performance	Test Condition	Test Method	BASF GERMANY/B 4406
Melting temperature		ISO 3146	223 °C
RTI Imp	3.0mm	UL 746	130 °C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1500 mm/mm.℃
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	165 °C
Melting temperature		ASTM D3418	223 °C
RTI Str	0.75mm	UL 746	140 °C
RTI Imp	1.5mm	UL 746	130 °C
RTI Elec	3.0mm	UL 746	125 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	60.0 °C
RTI Str	3.0mm	UL 746	140 °C
Linear coefficient of thermal expansion	MD	ASTME831	9E-05 cm/cm/°C
RTI Imp	0.75mm	UL 746	130 °C
RTI Str	1.5mm	UL 746	140 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	170 °C
Hot deformation temperature		1.8MPa,Unannealed	ASTM D648	80.0 °C
RTI Elec	1.5mm	UL 746	125 °C
Linear coefficient of thermal expansion	MD		5.5E-05 cm/cm/°C
Combustibility (rate)		UL 94	V-0
RTI Elec	0.75mm	UL 746	125 °C
Electrical performance	Test Condition	Test Method	BASF GERMANY/B 4406
Dielectric constant	100Hz	IEC 60250	3.30
Dissipation factor	100Hz	IEC 60250	0.011
Volume resistivity	1.50mm	ASTM D257	>1.0E+15 ohms
Volume resistivity			IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.017
Surface resistivity		IEC 60093	1E+13 ohms
Dielectric constant	1MHz	IEC 60250	3.30
Compared to the anti leakage trace index		IEC 60112	PLC 2
Volume resistivity		ASTM D257/IEC 60093	1E 14 Ω.cm
other	Test Condition	Test Method	BASF GERMANY/B 4406
purpose			高刚度和强度、尺寸稳定性、低吸水率和耐化学性.耐侯性和抗热老化性；应用于高性能领域.如不同工业部门中的承重部分
flammability	Test Condition	Test Method	BASF GERMANY/B 4406
UL flame retardant rating	0.40mm	UL 94	V-0
		1.5mm	UL 94	V-0
		0.75mm	UL 94	V-0
		3.0mm	UL 94	V-0
Physical properties	Test Condition	Test Method	BASF GERMANY/B 4406
Shrinkage rate	MD：3.18mm		0.15 %
density		ASTM D792/ISO 1183	1450
Water absorption rate		ASTM D570/ISO 62	0.4 %
Viscosity value	降低的粘度	ISO 1628	122.0 ml/g
Water absorption rate	Equilibrium,50%RH	ASTM D570	0.25 %
Water absorption rate		Equilibrium,23°C,50%RH	ISO 62	0.25 %
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	30.0 cm3/10min
Water absorption rate	Saturation,23°C	ISO 62	0.40 %
Water absorption rate		Saturation	ASTM D570	0.40 %
impact performance	Test Condition	Test Method	BASF GERMANY/B 4406
Impact strength of simply supported beam without notch	23°C	ISO 179	50 kJ/m²