Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT B 4406 BASF GERMANY
Ultradur®
Electrical components,switch,Laptop case
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B 4406 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B 4406 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| dielectric constant | 100Hz | IEC 60250 | 3.30 |
| Volume resistivity | 1.50mm | ASTM D257 | 1E+13 ohms |
| IEC 60093 | >1.0E+15 ohms·cm | ||
| Dissipation Factor | 100Hz | IEC 60250 | 0.011 |
| Volume resistivity | 1.50mm | ASTM D257 | >1.0E+15 ohms·cm |
| dielectric constant | 1MHz | IEC 60250 | 3.30 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Volume resistivity | ASTM D257/IEC 60093 | 1E 14 Ω.cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.017 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B 4406 |
|---|---|---|---|
| Tensile creep modulus | 1hr | ISO 899-1 | 1800 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 65.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 3.9 % |
| Tensile modulus | 23°C | ISO 527-2 | 3000 Mpa |
| ASTM D638/ISO 527 | 3000 kg/cm²(MPa)[Lb/in²] | ||
| Nominal tensile fracture strain | -40°C | ISO 527-2 | 3.3 % |
| tensile strength | 屈服,23°C | ASTM D638 | 65.0 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 3.9 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 3.5 % |
| other | Test Condition | Test Method | BASF GERMANY/B 4406 |
|---|---|---|---|
| purpose | 高刚度和强度、尺寸稳定性、低吸水率和耐化学性.耐侯性和抗热老化性；应用于高性能领域.如不同工业部门中的承重部分 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/B 4406 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1450 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.4 % |
| flammability | Test Condition | Test Method | BASF GERMANY/B 4406 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 | |
| 0.40mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | BASF GERMANY/B 4406 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.15 % | |
| Water absorption rate | 饱和 | ASTM D570 | 0.40 % |
| 平衡,50%RH | ASTM D570 | 0.25 % | |
| 平衡,23°C,50%RH | ISO 62 | 0.25 % | |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 30.0 cm3/10min |
| Viscosity value | 降低的粘度 | ISO 1628 | 122.0 ml/g |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B 4406 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| Combustibility (rate) | UL 94 | V-0 | |
| RTI Str | 0.75mm | UL 746 | 140 °C |
| RTI Imp | 1.5mm | UL 746 | 130 °C |
| melting temperature | ASTM D3418 | 223 °C | |
| RTI Elec | 3.0mm | UL 746 | 125 °C |
| RTI Imp | 3.0mm | UL 746 | 130 °C |
| melting temperature | ISO 3146 | 223 °C | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1500 mm/mm.℃ | |
| RTI Elec | 0.75mm | UL 746 | 125 °C |
| RTI Imp | 0.75mm | UL 746 | 130 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 165 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 170 °C | |
| Linear coefficient of thermal expansion | MD | 5.5E-05 cm/cm/°C | |
| RTI Str | 1.5mm | UL 746 | 140 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 60.0 °C |
| RTI Str | 3.0mm | UL 746 | 140 °C |
| RTI Elec | 1.5mm | UL 746 | 125 °C |
| Linear coefficient of thermal expansion | MD | ASTME831 | 9E-05 cm/cm/°C |