Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC XHT3141-BK1G412T SABIC INNOVATIVE NANSHA
LEXAN™ 
Automotive interior parts
High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT3141-BK1G412T
Charpy Notched Impact Strength23°CISO 179/1eA11 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376368.0 J
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT3141-BK1G412T
Tensile modulus--2ASTM D6382700 Mpa
tensile strength 屈服3ASTM D63870.0 Mpa
elongation断裂3ASTM D63870 %
断裂ISO 527-2/5070 %
Flexural modulus--5ISO 1782500 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D790120 Mpa
--5,6ISO 17880.0 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7902600 Mpa
tensile strength 断裂ISO 527-2/5060.0 Mpa
屈服ISO 527-2/5070.0 Mpa
elongation屈服ISO 527-2/506.0 %
屈服3ASTM D6386.0 %
tensile strength 断裂3ASTM D63855.0 Mpa
Tensile modulus--ISO 527-2/12500 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT3141-BK1G412T
dielectric strength3.20 mm, in OilASTM D14923 KV/mm
Volume resistivityASTM D257> 1.0E+17 ohms·cm
Dissipation Factor100 HzASTM D1500.031
dielectric constant100 HzASTM D1502.90
Surface ResistivityASTM D257> 1.0E+17 ohms
dielectric constant1 MHzASTM D1502.80
Hot wire ignition (HWI)UL 746PLC 3
Compared to the Leakage Tracking Index (CTI)UL 746PLC 3
Dissipation Factor1 MHzASTM D1500.011
High arc combustion index (HAI)UL 746PLC 0
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT3141-BK1G412T
UL flame retardant rating3.0 mmUL 94HB
Hot filament ignition temperature3.0 mmIEC 60695-2-13875 °C
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
UL flame retardant rating1.5 mmUL 94HB
Metallic haze起始内部方法165 °C
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT3141-BK1G412T
Water absorption rate平衡, 23°C, 50% RHISO 620.30 %
melt mass-flow rate330°C/2.16 kgASTM D123833 g/10 min
Water absorption rate饱和, 23°CISO 620.30 %
Melt volume flow rate330°C/2.16 kgISO 113330.0 cm3/10min
Shrinkage rate3.20 mm，Flow内部方法0.60 - 0.90 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT3141-BK1G412T
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8316.0E-5 cm/cm/°C
thermal conductivity25°CASTM C1770.20 W/m/K
Linear coefficient of thermal expansion横向 : -40°CISO 11359-26.0E-5 cm/cm/°C
Heat distortion temperature0.45 MPa, 未退火, 3.20 mm，HDTASTM D648166 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDTISO 75-2/Bf164 °C
RTIUL 746150 °C
vicat--ASTM D152510170 °C
--ISO 306/B50168 °C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDTISO 75-2/Af152 °C
RTI ImpUL 746130 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8316.0E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648156 °C
RTI ElecUL 746150 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT3141-BK1G412T
screw speed40 to 90 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature290 to 350 °C
drying temperature135 °C
Suggested injection volume40 to 60 %
drying time4.0 to 6.0 hr
Temperature in the middle of the barrel280 to 340 °C
Temperature at the rear of the barrel270 to 330 °C
Exhaust hole depth0.025 to 0.080 mm
Temperature at the front of the material cylinder290 to 350 °C
Back pressure0.300 to 0.700 Mpa
Temperature95 to 130 °C
Spray nozzle temperature285 to 345 °C