Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-765 WH TAIWAN CHIMEI
POLYLAC®
Fitness equipment,Electrical applications,Home appliance components
High mobility,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN CHIMEI/PA-765 WH |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 23 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 210 J/m |
| 23°C,6.40mm | ASTM D256 | 180 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.0 kJ/m² |
| 23°C | ISO 180/1A | 22 kJ/m² |
| hardness | Test Condition | Test Method | TAIWAN CHIMEI/PA-765 WH |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 100 |
| Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-765 WH |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 37.0 Mpa |
| elongation | 断裂4 | ASTM D638 | 15 % |
| bending strength | --5 | ASTM D790 | 60.7 Mpa |
| tensile strength | 屈服4 | ASTM D638 | 38.1 Mpa |
| bending strength | --6 | ISO 178 | 55.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 10 % |
| Flexural modulus | --6 | ISO 178 | 1800 Mpa |
| --5 | ASTM D790 | 2070 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 28.0 Mpa |
| flammability | Test Condition | Test Method | TAIWAN CHIMEI/PA-765 WH |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| 1.0mm | UL 94 | V-1 | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TAIWAN CHIMEI/PA-765 WH |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.19 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 5.0 g/10min |
| Shrinkage rate | ISO 294-4 | 0.30-0.60 % | |
| density | --3 | ASTM D792 | 1.19 g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 50.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PA-765 WH |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 73.0 °C |
| vicat | -- | ASTM D15257 | 90.0 °C |
| -- | ISO 306/A50 | 91.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 74.0 °C |
| vicat | -- | ISO 306/B50 | 78.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTMD648 | 83.0 °C |