PPS 1130A64 JAPAN POLYPLASTIC
DURAFIDE®
Fiber grade
enhance,Flame retardant,High mobility,standard,High temperature resistan,Low flash
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A64 |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 105 M（Scale） |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A64 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 230 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 10500 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 23°C | ISO 178 | 230 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 10500 Mpa |
| elongation at break | ASTM D638/ISO 527 | 1.9 % | |
| 23°C | ISO 527-2 | 1.9 % | |
| tensile strength | ASTM D638/ISO 527 | 170 kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO 527-2 | 170 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A64 |
|---|---|---|---|
| dielectric constant | 23°C | IEC 60250 | 4.2 1kHz |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 125 V |
| 23°C | IEC 60250 | 1E-03 1kHz | |
| dielectric constant | 23°C | IEC 60250 | 4.2 1MHz |
| Dissipation Factor | 23°C | IEC 60250 | 2E-03 1MHz |
| dielectric strength | 3mm | IEC 60243-1 | 15 KV/mm |
| Volume resistivity | ASTM D257/IEC 60093 | 8.0 x 10^15 Ω.cm | |
| IEC 60093 | 8E+15 Ω.cm | ||
| Dissipation Factor | 耐电弧性 | IEC 61621 | 123 S |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A64 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.57 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.01 % |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A64 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 1.50mm | |
| UL -94 | V-0 0.81mm | ||
| UL -94 | V-0 3.00mm | ||
| UL -94 | V-0 0.38mm |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A64 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.04 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A64 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 265 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-02 cm/cm/°C |
| TD | ISO 11359-2 | 4E-02 cm/cm/°C | |
| ASTM D696/ISO 11359 | - mm/mm.℃ |