PA66 Nylux 66-NAT KMI Group, Inc.
--
currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | KMI Group, Inc./Nylux 66-NAT |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 5.5 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 5.4 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
Mechanical properties | Test Condition | Test Method | KMI Group, Inc./Nylux 66-NAT |
---|---|---|---|
Tensile modulus | ISO 527-2 | 3200 MPa | |
Tensile strain | 断裂 | ISO 527-2 | 50 % |
屈服 | ISO 527-2 | 4.2 % | |
tensile strength | 屈服 | ISO 527-2 | 82.0 MPa |
Flexural modulus | ISO 178 | 2900 MPa | |
bending strength | ISO 178 | 95.0 MPa |
Electrical performance | Test Condition | Test Method | KMI Group, Inc./Nylux 66-NAT |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
dielectric strength | IEC 60243-1 | 32 kV/mm | |
Volume resistivity | IEC 60093 | 4E+14 ohms·cm | |
Surface Resistivity | IEC 60093 | 3E+14 ohms |
physical property | Test Condition | Test Method | KMI Group, Inc./Nylux 66-NAT |
---|---|---|---|
Shrinkage rate | MD:2.00mm | ISO 294-4 | 1.9 % |
Water absorption rate | 23°C,24hr | ISO 62 | 1.4 % |
平衡,23°C,50%RH | ISO 62 | 2.7 % | |
density | ISO 1183 | 1.14 g/cm³ | |
Shrinkage rate | TD:2.00mm | ISO 294-4 | 1.8 % |
Thermal performance | Test Condition | Test Method | KMI Group, Inc./Nylux 66-NAT |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | 204 °C | |
Linear coefficient of thermal expansion | MD | 8E-05 cm/cm/°C | |
melting temperature | 261 °C |