Product Name / Manufacturer / Model

Brand

Typical Applications

Properties

Color

Form

Processing Methods

Grade

Filler

Recycled Content

Certificates

Reference Price

PC
PC SABIC INNOVATIVE SHANGHAI SLX2432T-NA9D082T
US$ 8,340 / MT
FOB Shanghai port, China
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T
elongationBreakASTM D638110 %
bending strengthISO 178105 Mpa
Bending modulus50.0mmSpanASTM D7902500 Mpa
Tensile modulusISO 527-2/12550 Mpa
ASTM D6382550 Mpa
tensile strengthBreakISO 527-2/5069.0 Mpa
YieldISO 527-2/5065.0 Mpa
Tensile strainBreakISO 527-2/50110 %
bending strengthYield,50.0mmSpanASTM D790105 Mpa
tensile strengthBreakASTM D63872.0 Mpa
YieldASTM D63867.0 Mpa
Bending modulusISO 1782500 Mpa
Tensile strainYieldISO 527-2/506.0 %
elongationYieldASTM D6386.0 %
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T
Vicat softening temperature--ISO 306/B50135 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af116 °C
1.8MPa,Unannealed,3.20mmASTM D648118 °C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-26.7E-05 cm/cm/°C
MD：-40to40°CASTME8316.7E-05 cm/cm/°C
TD：-40to40°CASTME8316.5E-05 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf130 °C
Vicat softening temperatureASTM D152510135 °C
--ISO 306/B120137 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648130 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-26.5E-05 cm/cm/°C
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T
Burning wire flammability index1.6mmIEC 60695-2-12960 °C
Extreme Oxygen IndexISO 4589-238 %
UL flame retardant rating1.5mmUL 94V-2
impact performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T
Charpy Notched Impact Strength-30°CISO 179/1eA15 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A25 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Dart impact-40°C,TotalEnergyASTM D376385.0 J
Charpy Notched Impact Strength23°CISO 179/1eA30 kJ/m²
Dart impact23°C,TotalEnergyASTM D376377.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
optical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T
transmissivity2540μmASTM D100384.0 %
turbidity2540μmASTM D10030.80 %
Refractive indexASTM D5421.590
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T
melt mass-flow rate300°C/1.2kgASTM D123810 g/10min
Outdoor applicabilityUL 746Cf1
Water absorption rate24hrASTM D5700.12 %
Equilibrium,23°C,50%RHISO 620.17 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 620.25 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11339.00 cm3/10min

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China