Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC SLX2432T-NA9D082T SABIC INNOVATIVE SHANGHAI
LEXAN™
Electronic and Electrical、Lighting applications、Plastic bag、Outdoor applications、Lawn garden equipment
Aging resistance、UV resistance、Antistatic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 30 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 77.0 J |
| -40°C,TotalEnergy | ASTM D3763 | 85.0 J | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 25 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2550 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| tensile strength | 断裂 | ASTM D638 | 72.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 69.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2500 Mpa |
| Tensile modulus | ASTM D638 | 2550 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 105 Mpa |
| elongation | 断裂 | ASTM D638 | 110 % |
| bending strength | ISO 178 | 105 Mpa | |
| Flexural modulus | ISO 178 | 2500 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 67.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 0.80 % |
| refractive index | ASTM D542 | 1.590 | |
| transmissivity | 2540µm | ASTM D1003 | 84.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T |
|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| Limiting Oxygen Index | ISO 4589-2 | 38 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.12 % |
| Outdoor applicability | UL 746C | f1 | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.17 % |
| 饱和,23°C | ISO 62 | 0.25 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SLX2432T-NA9D082T |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 130 °C |
| vicat | -- | ISO 306/B120 | 137 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.5E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 130 °C |
| vicat | -- | ISO 306/B50 | 135 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 6.7E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 116 °C |
| vicat | ASTM D152510 | 135 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 118 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |