PC LUX9612G-WH8A490X SABIC INNOVATIVE NANSHA
--
Lighting applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9612G-WH8A490X
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Dart impact23°C,TotalEnergyASTM D376370.0 J
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Multi axis Instrumented Impact EnergyISO 6603-2130 J
Suspended wall beam without notch impact strength23°CASTMD4812无断裂
Impact strength of cantilever beam gap23°CISO 180/1A40 kJ/m²
Suspended wall beam without notch impact strength-30°C5ISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9612G-WH8A490X
Rockwell hardnessR级ASTM D785118
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9612G-WH8A490X
Tensile modulusISO 527-2/12230 Mpa
elongation屈服ASTM D6386.0 %
tensile strength 断裂ASTM D63865.0 Mpa
Tensile strain屈服ISO 527-2/506.0 %
tensile strength 断裂ISO 527-2/5058.0 Mpa
Flexural modulus50.0mm跨距ASTM D7902160 Mpa
tensile strength 屈服ISO 527-2/5062.0 Mpa
Tensile modulusASTM D6382300 Mpa
elongation断裂ASTM D63880 %
bending strength屈服,50.0mm跨距ASTM D79095.0 Mpa
ISO 17895.0 Mpa
Flexural modulusISO 1782250 Mpa
tensile strength 屈服ASTM D63862.0 Mpa
Tensile strain断裂ISO 527-2/5075 %
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9612G-WH8A490X
Dissipation Factor50HzASTM D1509E-04
60HzASTM D1509E-04
dielectric constant60HzASTM D1503.17
50HzASTM D1503.17
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dissipation Factor1MHzASTM D1500.010
High arc combustion index (HAI)HAIUL 746PLC 1
Hot wire ignition (HWI)HWIUL 746PLC 3
dielectric constant1MHzASTM D1502.96
dielectric strength3.20mm,inAirASTM D14915 KV/mm
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 3
optical performance Test ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9612G-WH8A490X
refractive indexISO 4891.586
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9612G-WH8A490X
Burning wire flammability index0.8mmIEC 60695-2-12750 °C
1.5mmIEC 60695-2-12850 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13850 °C
1.5mmIEC 60695-2-13850 °C
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
UL flame retardant rating1.5mmUL 94V-0
0.30mmUL 94V-2
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9612G-WH8A490X
Shrinkage rateMD：3.20mm内部方法0.60-0.80 %
Outdoor applicabilityUL 746Cf2
Water absorption rate平衡,23°C,50%RHISO 620.15 %
Melt volume flow rate300°C/1.2kgISO 11337.00 cm3/10min
Water absorption rate饱和,23°CISO 620.35 %
平衡,100°CASTM D5700.58 %
melt mass-flow rate300°C/1.2kgASTM D12387.0 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9612G-WH8A490X
vicatASTM D152510140 °C
Heat distortion temperature1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af123 °C
RTIUL 746125 °C
RTI StrUL 746125 °C
specific heatASTMC3511260 J/kg/°C
Linear coefficient of thermal expansionMD:-40到40°CASTME8316.8E-05 cm/cm/°C
Heat distortion temperature0.45MPa,Unannealed,64.0mmSpan，HDTISO 75-2/Bf135 °C
0.45MPa,未退火,64.0mm跨距，HDTISO 75-2/Bf135 °C
vicat--ISO 306/B120142 °C
thermal conductivityASTMC1770.20 W/m/K
Linear coefficient of thermal expansionTD:-40到40°CASTME8316.7E-05 cm/cm/°C
vicat--ISO 306/B50141 °C
RTI ImpUL 746115 °C
Heat distortion temperature1.8MPa,Unannealed,64.0mmSpan，HDTISO 75-2/Af123 °C
1.8MPa,未退火,3.20mm，HDTASTM D648123 °C
ball-indentation hardness125°CIEC 60695-10-2Pass
RTI ElecUL 746125 °C