PA66 Alloy RAMLLOY B001 POLYRAM ISRAEL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY B001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 30 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 670 J/m |
| 23°C | ISO 180 | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY B001 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 180 % |
| Tensile modulus | ASTM D638 | 1800 MPa | |
| ISO 527-2 | 1800 MPa | ||
| Tensile strain | 断裂 | ISO 527-2 | 180 % |
| Flexural modulus | ASTM D790 | 2000 MPa | |
| tensile strength | 屈服 | ASTM D638 | 50.0 MPa |
| 屈服 | ISO 527-2 | 50.0 MPa | |
| Flexural modulus | ISO 178 | 2000 MPa | |
| bending strength | ASTM D790 | 70.0 MPa | |
| ISO 178 | 70.0 MPa |
| flammability | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY B001 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY B001 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 1.3 % | |
| melt mass-flow rate | 235°C/5.0kg | ASTM D1238 | 10 g/10min |
| Water absorption rate | 饱和 | ASTM D570 | 3.3 % |
| 平衡 | ASTM D570 | 1.3 % | |
| 饱和,23°C | ISO 62 | 3.3 % | |
| density | ASTM D792 | 1.03to1.05 g/cm³ | |
| ISO 1183 | 1.03to1.05 g/cm³ | ||
| melt mass-flow rate | 235°C/10.0kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY B001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 75.0 °C |
| melting temperature | ISO 11357-3 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 130 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 130 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C | |
| melting temperature | ASTM D3418 | 220 °C |