PLA F 1130 FKuR Kunststoff GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FKuR Kunststoff GmbH/ F 1130 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 24°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | 24°C | ISO 179/1eA | 无断裂 |
| film | Test Condition | Test Method | FKuR Kunststoff GmbH/ F 1130 |
|---|---|---|---|
| Nitrogen permeation rate | 45.0µm | DIN 53380-2 | 160 cm³/m²/bar/24hr |
| OTr | 45.0µm | ISO 15105-2 | 850 cm³/m²/bar/24hr |
| Water Vapor Transmission Rate | 45µm | ISO 15106-3 | 70 g/m²/24hr |
| Mechanical properties | Test Condition | Test Method | FKuR Kunststoff GmbH/ F 1130 |
|---|---|---|---|
| bending strength | 3.5%应变 | ISO 178 | 9.00 MPa |
| Tensile modulus | ISO 527-2 | 390 MPa | |
| tensile strength | 屈服 | ISO 527-2 | 17.0 MPa |
| Flexural modulus | ISO 178 | 370 MPa | |
| Tensile strain change rate | ISO 527 | >300 % |
| physical property | Test Condition | Test Method | FKuR Kunststoff GmbH/ F 1130 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 1.50to4.00 cm³/10min |
| Apparent density | ISO 60 | 0.83 g/cm³ | |
| density | ISO 1183 | 1.40 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.0to5.0 g/10min |
| Thermal performance | Test Condition | Test Method | FKuR Kunststoff GmbH/ F 1130 |
|---|---|---|---|
| vicat | ISO 306/A | 89.0 °C | |
| melting temperature | ISO 3146 | >155 °C |