Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 AKV35HRH2.0 LANXESS GERMANY
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/AKV35HRH2.0 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 65 kJ/m² |
| 23°C | ISO 180/1U | 75 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 85 kJ/m² |
| -30°C | ISO 179/1eU | 75 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/AKV35HRH2.0 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA66.GHRW.14-110.GF30 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/AKV35HRH2.0 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.1 % |
| Flexural modulus | 23°C | ISO 178/A | 10700 Mpa |
| bending strength | 3.5%Strain | ISO 178/A | -- Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 195 Mpa |
| bending strength | 23°C | ISO 178 | 305 Mpa |
| 23°C | ASTM D790 | 290 Mpa | |
| FlexuralStrainatFlexuralStrength6(23°C) | 3.8 % | ||
| Tensile modulus | 23°C | ASTM D638 | 11000 Mpa |
| 23°C | ISO 527-2/1 | 11500 Mpa | |
| tensile strength | 断裂,23°C | ASTM D638 | 190 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 10000 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 3.0 % |
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/AKV35HRH2.0 |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | IEC 60250 | 4.00 |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| 23°C,3.00mm | IEC 60243-1 | 40 KV/mm | |
| dielectric constant | 23°C,1MHz | IEC 60250 | 4.00 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.60 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.90 |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 6E-03 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 0.010 |
| 23°C,1MHz | IEC 60250 | 4.0E-30.015 |
| flammability | Test Condition | Test Method | LANXESS GERMANY/AKV35HRH2.0 |
|---|---|---|---|
| Burning Behavior | >1.00mm | ISO 3795 | passed |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LANXESS GERMANY/AKV35HRH2.0 |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.090 % |
| MD:300°C,2.00mm2 | ISO 294-4 | 0.38 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.7 % |
| 饱和,23°C | ISO 62 | 5.2 % | |
| Shrinkage rate | TD:300°C,2.00mm2 | ISO 294-4 | 1.1 % |
| MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.060 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/AKV35HRH2.0 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| vicat | -- | ISO 306/B120 | 255 °C |
| Heat distortion temperature | 0.45MPa,未退火,4.00mm，HDT | ASTM D648 | >249 °C |
| 1.8MPa,未退火,4.00mm，HDT | ASTM D648 | >249 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 250 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 245 °C |
| vicat | -- | ISO 306/B50 | >230 °C |
Contact Us
Get App