PP PPH1S05 M403 H-4166 Repol Engineering Plastics
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Repol Engineering Plastics/PPH1S05 M403 H-4166 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Repol Engineering Plastics/PPH1S05 M403 H-4166 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 4500 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 40.0 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 3.0 kJ/m2 |
| Flexural modulus | ISO 178 | 2200 MPa | |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 40 kJ/m2 |
| bending strength | ISO 178 | 50.0 MPa |
| physical property | Test Condition | Test Method | Repol Engineering Plastics/PPH1S05 M403 H-4166 |
|---|---|---|---|
| density | ISO 1183/A | 1.20 g/cm³ | |
| melt mass-flow rate | 230℃/2.16 kg | ISO 1133 | 5.0 g/10min |
| density | ISO 1183/A | 1.2 g/cm3 | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 5.0 g/10min |
| Thermal performance | Test Condition | Test Method | Repol Engineering Plastics/PPH1S05 M403 H-4166 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 100 ℃ |