PBT T08 200 DSM HOLAND
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/T08 200 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/T08 200 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2550 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| Tensile strain | 屈服 | ISO 527-2 | 3.5 % |
| tensile strength | 屈服 | ISO 527-2 | 55.0 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/T08 200 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 27 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | DSM HOLAND/T08 200 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | DSM HOLAND/T08 200 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.18 % |
| 饱和,23°C | ISO 62 | 0.45 % | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 10.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/T08 200 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 170 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 55.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |
| TD | ISO 11359-2 | 9E-05 cm/cm/°C |