PA6 B3S(粉) BASF SHANGHAI
Ultramid®
Thin walled components、parts、Shell
crystallization、High mobility、Fast forming cycle、Oil resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF SHANGHAI/B3S(粉) |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 250 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180 | 3.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179 | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 200 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/B3S(粉) |
|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 3400 Mpa |
| Flexural modulus | 23°C | ISO178 | 2900 Mpa |
| Tensile strain | 屈服,23°C | ISO527-2 | 3.8 % |
| Nominal tensile fracture strain | 23°C | ISO527-2 | 10 % |
| Tensile stress | 屈服,23°C | ISO527-2 | 88.0 Mpa |
| physical property | Test Condition | Test Method | BASF SHANGHAI/B3S(粉) |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 3.0 % |
| 饱和,23°C | ISO62 | 9.5 % | |
| Melt volume flow rate | 275°C/5.0kg | ISO1133 | 175 cm3/10min |
| density | ISO1183 | 1.13 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/B3S(粉) |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/A | 65.0 °C | |
| ISO3146 | 220 °C |