PC FL900 SABIC INNOVATIVE US
LEXAN™
Casters,Household appliances,Household appliances,Automotive sector
High temperature resistan,Anti creep,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/FL900 |
|---|---|---|---|
| foaming | 内部方法 | 10 % | |
| Dart impact | 23°C | 内部方法 | 51.5 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/FL900 |
|---|---|---|---|
| bending strength | Yield,6.40mm | ASTM D790 | 89.6 Mpa |
| Flexural modulus | 6.40mm | ASTM D790 | 2790 Mpa |
| elongation | 断裂,6.35mm | ASTM D638 | 6.2 % |
| tensile strength | Yield,6.35mm | ASTM D638 | 50.3 Mpa |
| foaming | 内部方法 | 10 % | |
| Tensile modulus | 6.40mm | ASTM D638 | 2450 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/FL900 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Dissipation Factor | 100Hz | ASTM D150 | 1.2E-03 |
| Volume resistivity | ASTM D257 | 2.5E+17 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 6.1E-03 |
| Surface Resistivity | ASTM D257 | >1.1E+17 ohms | |
| foaming | 内部方法 | 20 % | |
| dielectric constant | 1MHz | ASTM D150 | 2.12 |
| arc resistance | ASTM D495 | PLC7 | |
| dielectric constant | 100Hz | ASTM D150 | 2.22 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/FL900 |
|---|---|---|---|
| Radiation board grade | UL | YES | |
| UL flame retardant rating | 6.0mm | UL 94 | V-0 |
| foaming | 内部方法 | 750 kg/m3 | |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| 3.9mm | UL 94 | V-1 | |
| Limiting Oxygen Index | ASTM D2863 | 40 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/FL900 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.16 % |
| Outdoor applicability | UL 746C | f2 | |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.35 % |
| Shrinkage rate | MD：6.40mm | 内部方法 | 0.50-0.70 % |
| foaming | 内部方法 | 10 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/FL900 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 127 °C |
| foaming | 内部方法 | 10 % | |
| thermal conductivity | ASTMC177 | 0.15 W/m/K | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 138 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Str | UL 746 | 80.0 °C | |
| specific heat | ASTMC351 | 1170 J/kg/°C | |
| RTI Elec | UL 746 | 80.0 °C |