PA66 CM3004-V0 TORAY JAPAN
Amilan®
OA device,Electrical appliances,Electrical components,Shell
Flame retardant,Halogen-free
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 140 |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 120 -- |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| Water absorption rate | （24小时）23°C | ASTM D-570 | 1.1 % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| tensile strength | 23°C，断裂 | ASTM D-638 | 12 kg/cm |
| 23°C | MPa | 85.0 65.0 | |
| Taber abraser | 1000Cycles | mg | 9.00to10.0 -- |
| Tensile strain | 断裂,23°C | % | 7.5 7.5 |
| bending strength | -40°C | ASTM D-790 | 1210 kg/cm |
| Tensile and flexural strength | 23°C | ASTM D-638 | 850 kg/cm |
| bending strength | 23°C | MPa | 125 70.0 |
| 80°C | MPa | 65.0 -- | |
| Flexural modulus | 23°C | MPa | 3500 1500 |
| Ezo De Wei Sheng | 无缺口1/2" 23°C | 5 kg.cm/cm | |
| Flexural modulus | 80°C | MPa | 1200 -- |
| bending strength | -40°C | MPa | 170 -- |
| Flexural modulus | -40°C | ASTM D-790 | 34500 kg/cm |
| tensile strength | 80°C | MPa | 45.0 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| arc resistance | 1/8" | ASTM D-150 | 127 |
| dielectric constant | 23°C,50Hz | 5.20 -- | |
| Compared to the Leakage Traceability Index (CTI) | 导热率温度指表 | UL 746 | 600 V |
| arc resistance | sec | 127 -- | |
| Dissipation Factor | 23°C,50Hz | 0.070 -- | |
| Volume resistivity | ASTM D-257 | V-0 Ω.cm | |
| dielectric strength | 1/8" 短时间 | ASTM D-149 | 17 KV/mm |
| Volume resistivity | ohms·cm | 1E+15 -- | |
| dielectric strength | kV/mm | 28 -- | |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | PLC 0 |
| other | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| characteristic | 阻燃级 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.18 |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | V-0 -- |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | % | 7.5 -- |
| Shrinkage rate | MD：3.00mm4 | % | 1.0-1.6 |
| Flame resistant grade | UL 94 | 113 | |
| Shrinkage rate | MD：1.00mm3 | % | 0.60-0.90 |
| Water absorption rate | 23°C,24hr | % | 1.1 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM3004-V0 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 244 -- |
| melting temperature | 差示扫描测热计DSC法 | 265 °C | |
| °C | 265 -- | ||
| Heat distortion temperature | 4.6kg/cm，HDT | ASTM D-648 | 244 °C |
| melting temperature | 265 ℃（℉） |