Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 D22 EVONIK GERMANY
VESTAMID®
Automotive Applications、pipeline
Easy to process、Thermal stability、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EVONIK GERMANY/D22 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30℃，完全断裂-22°F, Complete Break | ISO 179/1eA | 7 kJ/m² |
| Impact strength of simply supported beam without notch | 23℃23°C | ISO 179/1eU | No Break |
| -30℃-30°C | ISO 179/1eU | No Break | |
| Charpy Notched Impact Strength | 23℃，完全断裂73°F, Complete Break | ISO 179/1eA | 7 kJ/m² |
| Mechanical properties | Test Condition | Test Method | EVONIK GERMANY/D22 |
|---|---|---|---|
| Tensile strain | 屈服屈服 | ISO 527-2/1A | 4 % |
| tensile strength | 屈服屈服 | ISO 527-2/1A | 60 Mpa |
| Tensile modulus | ISO 527-2/1A | 2200 Mpa | |
| Tensile strain | 断裂断裂 | ISO 527-2/1A | > 50 % |
| Electrical performance | Test Condition | Test Method | EVONIK GERMANY/D22 |
|---|---|---|---|
| Dissipation Factor | 1 MHz1 MHz | IEC 60250 | 0.029 |
| dielectric strength | IEC 60243-1 | 27 KV/mm | |
| relative permittivity | 100 Hz100 Hz | IEC 60250 | 3.8 |
| Dissipation Factor | 100 Hz100 Hz | IEC 60250 | 0.023 |
| Volume resistivity | IEC 60093 | 1000000000000000 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 0 |
| relative permittivity | 1 MHz1 MHz | IEC 60250 | 3 |
| Flame retardant performance | Test Condition | Test Method | EVONIK GERMANY/D22 |
|---|---|---|---|
| UL flame retardant rating | 1.60 mm | UL 94 | HB |
| 3.20 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | EVONIK GERMANY/D22 |
|---|---|---|---|
| Shrinkage rate | MDFlow | ISO 294-4 | 1.3 % |
| Water absorption rate | 饱和，23℃饱和，23℃ | ISO 62 | 2.7 % |
| 平衡，23℃，50% RH平衡，23℃，50% RH | ISO 62 | 1 % | |
| Shrinkage rate | TDAcross Flow | ISO 294-4 | 1.1 % |
| Thermal performance | Test Condition | Test Method | EVONIK GERMANY/D22 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa，未退火264 psi, Unannealed，HDT | ISO 75-2/A | 60 °C |
| vicat | 熔融温度Melting Temperature 55 | ISO 11357-3 | 215 °C |
| Linear coefficient of thermal expansion | MD：23~55℃MD：23 到 55℃ | ISO 11359-2 | 0.00013 1/℃ |
| Heat distortion temperature | 1.8 MPa，未退火264 psi, Unannealed 147，HDT | ISO 75-2/A | 75 °C |