PC DCL-4532 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive components、Electronic and electrical、Sports equipment
Thermal stability、High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4532 BK |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 6.3E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 148 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 148 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 4.1E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 144 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 144 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 4.1E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4532 BK |
|---|---|---|---|
| Tensile Strain | 屈服 | ISO527-2 | 2.2 % |
| Tensile Elongation | 断裂 | ASTMD638 | 2.1 % |
| Flexural Modulus | ASTMD790 | 6210 Mpa | |
| Flexural Strength | 138 Mpa | ||
| Tensile Stress | 屈服 | ISO527-2 | 93.0 Mpa |
| Tensile Modulus | ISO527-2/1 | 7470 Mpa | |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.36 |
| Tensile Strength | 屈服 | ASTMD638 | 91.7 Mpa |
| Flexural Modulus | ISO178 | 6700 Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.37 |
| Tensile Elongation | 屈服 | ASTMD638 | 2.1 % |
| Specific Wear Rate | ASTMD3702Modified | 49.0 10^-10in^5-min/ft-lb-hr | |
| Tensile Strain | 断裂 | ISO527-2 | 2.2 % |
| Tensile Stress | 93.0 Mpa | ||
| Flexural Stress | ISO178 | 142 Mpa | |
| Tensile Modulus | ASTMD638 | 7580 Mpa | |
| Tensile Strength | 断裂 | 91.7 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4532 BK |
|---|---|---|---|
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.10 % |
| Modeling Shrinkage | MD：24小时 | ASTMD955 | 0.30to0.50 % |
| TD:24小时 | ISO294-4 | 0.54 % | |
| TD：24hr | ASTMD955 | 0.40to0.60 % | |
| MD:24小时 | ISO294-4 | 0.43 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4532 BK |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 18.6 J |
| 23°C | ISO180/1U | 29 kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 5.30 J | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 9.1 kJ/m² |