PC 141-111 PC vs. - Plastic Material Properties Comparison Chart at Plas.com

injection	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
Back pressure			0.300 to 0.700 Mpa
Temperature at the front of the material cylinder			295 to 315 °C
Screw speed			40 to 70 rpm
Mold temperature			70 to 95 °C
Processing (melt) temperature			295 to 315 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
Spray nozzle temperature			290 to 310 °C
Exhaust hole depth			0.025 to 0.076 mm
drying temperature			120 °C
Temperature in the middle of the barrel			280 to 305 °C
drying time			3.0 to 4.0 hr
Temperature at the rear of the barrel			270 to 295 °C
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
elongation	Break	ASTM D638	130 %
tensile strength	Break	ASTM D638	68.0 Mpa
elongation	Yield	ASTM D638	7.0 %
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0 mg
Bending modulus	50.0 mm Span	ASTM D790	2340 Mpa
tensile strength	Yield	ASTM D638	62.0 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	96.0 Mpa
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137 °C
Vicat softening temperature		ASTM D15255	154 °C
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	6.8E-5 cm/cm/°C
specific heat		ASTM C351	1250 J/kg/°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132 °C
thermal conductivity		ASTM C177	0.27 W/m/K
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
RTI		UL 746	130 °C
impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
Dart impact	23°C	ASTM D3029	169 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200 J/m
Dart impact	23°C, Energy at Peak	ASTM D3763	63.0 J
Impact strength of cantilever beam gap		ASTM D1822	577 kJ/m²
optical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
turbidity	2540 μm	ASTM D1003	1.0 %
transmissivity	2540 μm	ASTM D1003	88.0 %
Refractive index		ASTM D542	1.586
flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
Extreme Oxygen Index		ISO 4589-2	25 %
UL flame retardant rating	0.71 mm	UL 94	HB
Radiation board grade		UL Unspecified	TRUE
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
Compared to the anti leakage trace index		UL 746	PLC 2
Dissipation factor	50 Hz	ASTM D150	9.0E-4
		60 Hz	ASTM D150	9.0E-4
		1 MHz	ASTM D150	0.010
High voltage arc tracing rate		UL 746	PLC 2
Dielectric constant	1 MHz	ASTM D150	2.96
Dielectric strength	3.20 mm, in Air	ASTM D149	15 KV/mm
High arc combustion index		UL 746	PLC 1
Hot wire ignition		UL 746	PLC 2
Volume resistivity		ASTM D257	> 1.0E+17 ohms·cm
Dielectric constant	60 Hz	ASTM D150	3.17
Dielectric constant		50 kHz	ASTM D150	3.17
hardness	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness		M-Scale	ASTM D785	70
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/141-111
Water absorption rate	24 hr	ASTM D570	0.15 %
Water absorption rate		Equilibrium, 100°C	ASTM D570	0.58 %
Specific volume		ASTM D792	0.830 cm³/g
Outdoor applicability		UL 746C	f2
Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35 %
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	11 g/10 min