Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PA6 B3GK24 BK00564 BASF GERMANY

Ultramid®

Thin walled components,Plastic accessories,Shell,Application in the automotive field,Industrial components,Electrical enclosure

High mobility,Oil resistant,Filler: glass beads, fibe,30% filler by weight

Plastic Datasheets

Other performance	Test Condition	Test Method	BASF GERMANY/B3GK24 BK00564
impact strength	干/湿		5/25 J

thermal performance	Test Condition	Test Method	BASF GERMANY/B3GK24 BK00564
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	200 °C
		0.45MPa负荷，Dry		215 °C
		0.45MPa,Unannealed	ISO 75-2/B	215 °C
		1.8MPa,Unannealed	ISO 75-2/A	200 °C
		1.8MPa负荷，Dry		200 °C
		0.45MPa,Unannealed	ASTM D648	215 °C
Linear coefficient of thermal expansion	MD	ASTME831	1E-05 cm/cm/°C
		（23-80）℃，Dry		3.5-4 10
		MD		3.8E-05 cm/cm/°C
Maximum operating temperature			200 °C
Melting temperature		ASTM D3418	220 °C
Melting temperature			ISO 3146	220 °C
RTI Elec	3.0mm	UL 746	65.0 °C
		0.75mm	UL 746	65.0 °C
		1.5mm	UL 746	65.0 °C
RTI Imp	1.5mm	UL 746	65.0 °C
		3.0mm	UL 746	65.0 °C
		0.75mm	UL 746	65.0 °C
RTI Str	3.0mm	UL 746	65.0 °C
		1.5mm	UL 746	65.0 °C
		0.75mm	UL 746	65.0 °C
specific heat	Dry		1.4 J/(g.K)
thermal conductivity	Dry		0.34 W/(m.K)

mechanical properties	Test Condition	Test Method	BASF GERMANY/B3GK24 BK00564
Ball Pressure Test	干/湿		170/120 Mpa
Bending modulus	23°C	ASTM D790	4830 Mpa
Charpy Notched Impact Strength	+23℃,干/湿		40/90 KJ/m
		30℃干		39 KJ/m
		30℃，干/湿		5 KJ/m
Elongation at Break	干/湿，V=50mm/min		3.5/15 %
Fracture stress (V=50mm/min)	干/湿		110/65 Mpa
Impact strength of cantilever beam gap	+23℃，干/湿		5/8.5 KJ/m
Tensile creep modulus	1000h,湿		2000 Mpa
Tensile modulus	干/湿		6000/3000 Mpa
Tensile modulus		23°C	ISO 527-2	6000 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.5 %
tensile strength	Break,23°C	ISO 527-2	105 Mpa
tensile strength		Break,23°C	ASTM D638	110 Mpa
Tensile yield stress (V=50mm/min)	干/湿		110/65 Mpa

Electrical performance	Test Condition	Test Method	BASF GERMANY/B3GK24 BK00564
bending strength	干/湿		175/100 Mpa
Compared to the anti leakage trace index		IEC 60112	V
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 425
Dielectric constant	1MHz，干/湿		3.9/4.6 J/(g.K)
Dielectric constant		1MHz	IEC 60250	3.90
Dielectric strength	K20/P50，干/湿		135/53 KV/mm
Dissipation factor	1MHz	IEC 60250	0.020
Loss angle	1MHz，干/湿		0.02/0.07
Surface resistivity	干/湿		10 Ω
Volume resistivity		IEC 60093	1E+15 ohms·cm
		1.50mm	ASTM D257	1E+15 ohms·cm
		干/湿		10 Ω.cm

Physical properties	Test Condition	Test Method	BASF GERMANY/B3GK24 BK00564
density		ISO 1183	1.34 g/cm³
density			ASTM D792	1.34 g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	70.0 cm3/10min
Shrinkage rate	MD：3.18mm		0.40 %
Water absorption rate	Saturation	ASTM D570	6.6 %
		Equilibrium,23°C,50%RH	ISO 62	2.0 %
		Equilibrium,50%RH	ASTM D570	2.0 %
		Saturation,23°C	ISO 62	6.6 %

impact performance	Test Condition	Test Method	BASF GERMANY/B3GK24 BK00564
Charpy Notched Impact Strength	-30°C	ISO 179	5.0 kJ/m²
Charpy Notched Impact Strength		23°C	ISO 179	5.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	37 J/m
Impact strength of cantilever beam gap		-40°C	ASTM D256	32 J/m
Impact strength of simply supported beam without notch	-30°C	ISO 179	39 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179	40 kJ/m²

flammability	Test Condition	Test Method	BASF GERMANY/B3GK24 BK00564
UL flame retardant rating	0.75mm	UL 94	HB
		3.0mm	UL 94	HB
		1.5mm	UL 94	HB