PA6 B3WG5 BASF GERMANY
Ultramid®
Shell、Gears
Glass fiber reinforced、heat-resisting、Aging resistance、Filler: Glass fiber reinf、25% filler by weight、filler、Glass fiber reinforced ma、25%、Filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | BASF GERMANY/B3WG5 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 7.0 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 7.5 kJ/m² |
-40°C | ISO 180 | 6.5 kJ/m² |
Mechanical properties | Test Condition | Test Method | BASF GERMANY/B3WG5 |
---|---|---|---|
Tensile strain | 断裂,23°C | ISO 527-2 | 3.6 % |
tensile strength | 屈服,23°C | ISO 527-2 | 150 Mpa |
Tensile strain | 屈服,23°C | ISO 527-2 | 3.3 % |
Tensile modulus | 23°C | ISO 527-2 | 7700 Mpa |
tensile strength | 断裂,23°C | ISO 527-2 | 150 Mpa |
physical property | Test Condition | Test Method | BASF GERMANY/B3WG5 |
---|---|---|---|
density | ISO 1183 | 1.31 g/cm³ | |
Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 50.0 cm3/10min |
Thermal performance | Test Condition | Test Method | BASF GERMANY/B3WG5 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 210 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 200 °C | |
melting temperature | ISO 3146 | 220 °C |