PPO GFN1-701 SABIC INNOVATIVE NETHERLANDS
NORYL™
household electrical appl、Automotive interior parts、Water sports equipment
High mobility、Flame retardant、Glass fiber reinforced、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/GFN1-701 |
|---|---|---|---|
| Suspended wall beam gap impact strength 7 | -30°C | ISO180/1A | 9.4 kJ/m² |
| Simple supported beam without notch impact strength 6 | 23°C | ISO179/1eU | 35 kJ/m² |
| -30°C | ISO180/1U | 25 kJ/m² | |
| Suspended wall beam gap impact strength 7 | 23°C | ISO180/1A | 11 kJ/m² |
| 23°C | ISO180/1U | 28 kJ/m² | |
| Simple supported beam without notch impact strength 6 | -30°C | ISO179/1eU | 33 kJ/m² |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 21.7 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/GFN1-701 |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTMD785 | 104 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/GFN1-701 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 64.0 Mpa |
| bending strength | 屈服,50.0mm跨距4 | ASTMD790 | 116 Mpa |
| Tensile modulus | ISO527-2/1 | 4400 Mpa | |
| elongation | 断裂 | ASTMD638 | 3.0 % |
| bending strength | Yield,100mmSpan5 | ASTMD790 | 108 Mpa |
| Flexural modulus | 100mmSpan5 | ASTMD790 | 3590 Mpa |
| Bending stress | ISO178 | 122 Mpa | |
| tensile strength | 断裂 | ASTMD638 | 63.0 Mpa |
| Tensile modulus | ASTMD638 | 4350 Mpa | |
| Flexural modulus | ISO178 | 4160 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 3.0 % |
| Flexural modulus | 50.0mm跨距4 | ASTMD790 | 3840 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/GFN1-701 |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL746 | PLC 4 |
| dielectric constant | 1MHz | ASTMD150 | 2.90 |
| Arc resistance 9 | ASTMD495 | PLC7 | |
| Dissipation Factor | 1MHz | ASTMD150 | 1.4E-03 |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 5 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/GFN1-701 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/GFN1-701 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.50 % |
| Melt volume flow rate | 300°C/5.0kg | ISO1133 | 16.4 cm3/10min |
| Water absorption rate | 24hr | ASTMD570 | 0.060 % |
| melt mass-flow rate | 300°C/5.0kg | ASTMD1238 | 17 g/10min |
| Outdoor applicability | UL746C | f1 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/GFN1-701 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 122 °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 124 °C | |
| RTI Str | UL746 | 90.0 °C | |
| RTI Elec | UL746 | 90.0 °C | |
| MD：-40到40°C | ASTME831 | 5.1E-05 cm/cm/°C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 131 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 125 °C | |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 132 °C | |
| RTI Imp | UL746 | 90.0 °C | |
| vicat | -- | ISO306/B50 | 131 °C |
| -- | ISO306/B120 | 134 °C | |
| TD：-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C |