PEI CRS5001-1000 SABIC INNOVATIVE US
ULTEM™
Fitness equipment、Automotive sector、Bottle cap
High temperature resistan、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/CRS5001-1000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 2100 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/CRS5001-1000 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 123 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/CRS5001-1000 |
|---|---|---|---|
| Flexural modulus | 100mmSpan | ASTM D790 | 3100 Mpa |
| Tensile modulus | ASTM D638 | 2900 Mpa | |
| elongation | 断裂 | ASTM D638 | 60 % |
| bending strength | Yield,100mmSpan | ASTM D790 | 138 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| tensile strength | 屈服 | ASTM D638 | 100 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/CRS5001-1000 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Volume resistivity | ASTM D257 | 1.1E+17 ohms·cm | |
| Dissipation Factor | 100Hz | ASTM D150 | 1.7E-03 |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 18 KV/mm |
| Surface Resistivity | ASTM D257 | 5.8E+16 ohms | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC 5 | |
| dielectric constant | 100Hz | ASTM D150 | 3.12 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/CRS5001-1000 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/CRS5001-1000 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.16 % |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 4.2 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/CRS5001-1000 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 207 °C |
| RTI Imp | UL 746 | 160 °C | |
| RTI Str | UL 746 | 160 °C | |
| RTI Elec | UL 746 | 160 °C |