PPA HTN51G35HSLBK083 DUPONT BELGIUM
Zytel®
Automotive interior parts、Electrical appliances、Fitness equipment
Glass fiber reinforced、Thermal stability、Flame retardant、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT BELGIUM/HTN51G35HSLBK083 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 70 kJ/m² |
| -30°C | ISO179/1eU | 60 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT BELGIUM/HTN51G35HSLBK083 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 108 |
| R计秤 | ISO2039-2 | 124 |
| Supplementary Information | Test Condition | Test Method | DUPONT BELGIUM/HTN51G35HSLBK083 |
|---|---|---|---|
| Odor | VDA270 | 4.00 |
| Mechanical properties | Test Condition | Test Method | DUPONT BELGIUM/HTN51G35HSLBK083 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 210 Mpa |
| TensileCreepModule | 1hr | ISO899-1 | -- Mpa |
| Bending stress | ISO178 | 300 Mpa | |
| Poisson's ratio | ISO527 | 0.39 | |
| Tensile modulus | ISO527-2 | 12000 Mpa | |
| Flexural modulus | ISO178 | 10300 Mpa | |
| Tensile creep modulus | 1000hr | ISO899-1 | -- Mpa |
| Tensile strain | 断裂 | ISO527-2 | 2.4 % |
| Electrical performance | Test Condition | Test Method | DUPONT BELGIUM/HTN51G35HSLBK083 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | -- ohms | |
| 100Hz | IEC60250 | 4.00 | |
| CTI | IEC60112 | 600 V | |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC60243-1 | 36 KV/mm | |
| 1MHz | IEC60250 | 4.00 |
| flammability | Test Condition | Test Method | DUPONT BELGIUM/HTN51G35HSLBK083 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | 23 mm/min |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB |
| 0.9mm | IEC60695-11-10,-20 | HB | |
| 1.5mm | UL94 | HB | |
| Limiting Oxygen Index | ISO4589-2 | 24 % | |
| UL flame retardant rating | 0.9mm | UL94 | HB |
| physical property | Test Condition | Test Method | DUPONT BELGIUM/HTN51G35HSLBK083 |
|---|---|---|---|
| ThermalConductivityofMelt | 0.25 W/m/K | ||
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 4.5 % |
| Shrinkage rate | TD | ISO294-4 | 0.60 % |
| SpecificHeatCapacity of Melt | 1860 J/kg/°C | ||
| Shrinkage rate | MD | ISO294-4 | 0.20 % |
| Thermal performance | Test Condition | Test Method | DUPONT BELGIUM/HTN51G35HSLBK083 |
|---|---|---|---|
| MD：-40to23°C | ISO11359-2 | 1.8E-05 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 284 °C | |
| TD：-- | ISO11359-2 | 5.5E-05 cm/cm/°C | |
| 1.8MPa,未退火 | ISO75-2/A | 260 °C | |
| melting temperature | ISO11357-3 | 300 °C | |
| MD：-- | ISO11359-2 | 1.8E-05 cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 5.5E-05 cm/cm/°C |